•  Thickness: 0.07/0.08mm

•  Delivery temper: H16

•  Post brazing tensile strength>150Mpa

•  Post brazing yield strength>50Mpa

•  SWAAT test 4 weeks, performance is 10% better than 4343/AA3003/4343 (weight loss%)

High Strength Aluminum Foil for Fin Material

Aluminum alloy: 4343+3003+4343

Thickness: 0.0475-0.08mm+/-0.0025mm

Delivery temper: H14

Pre-brazed Tensile strength: 190-215MPa

Pre-brazed Elongation: Min1.0%(targetMin1.5%)

Pre-brazed Electrical Conductivity Min45%IACS

Post brazed tensile strength>135Mpa

Post-brazed Electrical Conductivity Min41.5%IACS

Post-brazed Grain size Min200μm

Post-brazed Electric Potential -750+/-10mV

Application: air conditioner, condenser 

Clad aluminum strip is widely used for manufacturing radiators and condensers

1)Core Alloy:  3003, etc

2)Cladding alloy:4343,4045,7072,5052 etc  4343/3003/4343

3)Cladding rate:4%-18%

4)Thickness: 0.07-0.30mm

5)Width: 16 - 1000mm (max)

6)Temper: H14 ,H16 etc

7)ID.:150mm,200mm,300mm,505mm

8)Normal OD.:900-1400mmm

9)Used:manufactuer radiators , condensers , evaporators ,heat exchanger, intercoolers , engine oil coolers etc 

10)Min Order: 3ton per size

11)Delivery Time: within 20-25days after receipt of your deposit

12)Packing : export standard packing